Electronic device and a manufacturing method for the same

ABSTRACT

A method for manufacturing a lead frame comprises the steps of covering, with a cover film, a die to which an electronic device is attached and a conducting section of a lead section to be electrically connected to the die, covering the whole of the die and lead section and the cover film with an inorganic protective film, and removing the cover film and the protective film formed over the cover film to partly expose the die and the conducting section for electric connection.

BACKGROUND OF THE INVENTION

1. Field of The Invention

The present invention relates to a method for manufacturing a lead frame or substrate, and in particular, to a method for manufacturing a lead frame or substrate for an electronic device such as a DIP or Flat Pack Package wherein a semiconductor or the like is mounted on the lead frame or substrate or the like in the electronic device and sealed in a molding material.

2. Description of the Prior Art

FIG. 1 shows the cross section of one part of a conventional electronic device. In FIG. 1, a lead frame 1 is made of a metal such as a copper, 42ALLOY or the like, and comprises a die 1a for mounting a semiconductor chip 3, and a lead section, that is an inner lead 1b and an outer lead 1c. The semiconductor chip 3 is die-attached e.g. by printing gold onto the surface of the die 1a, so that a gold-silicon alloy is formed at 300° C. to 400° C., and the semiconductor chip 3 is mounted using the gold-silicon alloy as an adhesive 5. In place of the gold-silicon alloy, it is also possible to use an adhesive such as an organic resin of a polyimide type or of an epoxy type, or a silver paste containing an organic material, or the like. An excess 5a of the adhesive is squeezed out during the mounting operation as shown in the drawing. The semiconductor chip 3 and the inner lead 1b are wire-bonded using a gold wire 9, after which the entire package is sealed in a plastic molding 7 with the exception of the outer lead 1c which is to be exposed.

When an organic adhesive is used as the adhesive 5, the adhesive in the flowable state is hardened by a chemical or thermochemical reaction, so that the semiconductor chip is mounted to the die 1a. This method has the advantages that it is inexpensive and easily adaptable to mass production. However, on the other hand, the adhesive 5 and the excess adhesive 5a are gradually vaporized and moved as indicated by the arrow 5b when heated in the range of 100° to 300° C., and an adhering material 5c is formed on the surface of the semiconductor chip 3 and lead frame 1. In addition, natural oxide and a suboxide 15 are formed on the lead frame 1. The adhering material 5c and the suboxide 15 are extremely easy to strip from the surface of the lead frame and therefore end up damaging the adherence of the subsequently-applied molding and protective film to the lead frame 1.

At the rear surface of the lead frame 1, it is easy for moisture to permeate into the plastic molding 7 from outside and to be accumulated thereon. When the device is usually dipped into molten solder, due to heat distortion or sudden expansion of vaporizing water, stress is produced causing the molding to expand. For this reason, cracks 11 and voids 13 are produced at the boundary between the die 1a and the molding 7 in areas where the adherence is poor.

SUMMARY OF THE INVENTION

An object of the present invention is to provide, with due consideration to the drawbacks of such conventional electronic devices, an electronic device with high reliability.

Another object of the present invention is to provide a method for manufacturing an electronic device of mold package type having an increased moisture resistance and adherence.

Another object of the present invention is to provide a package of the electronic device enclosed in a molding material with the prevention of the occurrence of cracks and voids in the package.

These objects are achieved in the present invention by the provision of a single-layer or multi-layer protective film of an inorganic material such as silicon nitride, silicon oxide, silicon carbide, or DLC (Diamond-Like Carbon), or the like, to cover the lead frame other than the electric contacts of the lead frame.

Specifically, in the present invention, the electric contacts of the lead frame (for example, parts which are wire-bonded, and parts which are attached to the semiconductor chip) are first covered with a cover film, then a protective film is formed of an inorganic material over the lead frame, after which, using the lift-off method, the cover film and the protective film formed over it are removed to once again expose the electric contacts.

In the present invention, the properties of organic resin molding materials, that is poor adherence to metals and good adherence to inorganic materials, are utilized. By means of the present invention, because the lead frame is covered in advance by a protective film, it is possible to avoid the soiling of the lead frame in the subsequent process in which the electronic parts are attached by means of an adhesive. In addition, because adhering material and suboxides are removed from the surface of the lead frame, the adhesrence of the material to the lead frame is improved. Also, the permeation of moisture through the undersurface of the package over a long period of time can be prevented, and there is no drop in reliability. Otherwise, the drop of reliability would be caused by water and chlorine in the organic resin, by the occurrence of a reaction between the water and chlorine and the metal of the die, resulting in the formation of suboxides. For this reason, there is no breakage, no matter how thin the molding, and no swelling from the application of heat when the package is mounted onto the PCB.

In addition, because the lead frame is protected by inorganic materials, the electronic device can be handled without so much carefulness, so that there is no drop in yield, and mass production is possible.

BRIEF DESCRIPTION OF THE DRAWINGS

These and other objects, features, and advantages of the present invention will become more apparent from the following description of the preferred embodiments taken in conjunction with the accompanying drawings, in which:

FIG. 1 is a vertical sectional view showing one part of a conventional plastic package semiconductor device after a moisture resistance test and solder test have been performed.

FIG. 2 is a vertical sectional view showing one part of a plastic type of semiconductor device using a lead frame in accordance with the present invention.

FIG. 3A to FIG. 3D are drawings showing the manufacturing process for a lead frame in accordance with the present invention.

FIG. 4A is a drawing showing generally a lead frame made in accordance with the present invention, wherein the lead frame is separated from the adjacent lead frames.

FIG. 4B is a drawing showing a substrate to which a plurality of the lead frames of FIG. 4A have been assembled.

FIG. 4C is a sectional view of substrate board which comprises a plurality of substrates assembled with a jig.

FIG. 5 is a drawing showing an external view of the plasma CVD device used in the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

FIG. 2 is a vertical sectional view showing a Flat Pack Package Type of a semiconductor device using the lead frame produced in accordance with the present invention. In FIG. 2, a lead frame 21 made from 42ALLOY or copper comprises a die 21a for die-attaching a semiconductor chip 23, and a lead section, that is an inner lead 21b and an outer lead 21c. The surface of the die 21a and the inner lead 21b are covered with an inorganic material 30 with the exception of the part on which the semiconductor chip 23 is mounted, and of a connection part 25 on which gold is printed for wire-bonding. The semiconductor chip 23 is electrically connected to a portion 25 of the inner lead 21b (where gold plating has been applied) through an aluminium pad 27 and a gold wire 29 for wire-bonding, and they are sealed by a molding 31.

Next, the process for manufacturing the lead frame of the present invention will be explained with reference to FIGS. 3A to 3D.

FIG. 3A is a sectional view of the lead frame which comprises a die 35 for mounting a semiconductor chip thereon, a lead section 37, a portion 39 on the lead section 37 for electrically connection by wire bonding, and a frame 41 for the lead frame. The die 35 is provided in a position lower than the lead section 37, so that a contact section provided on the chip is made on the same level or flush with the connecting portion 39. The lead frame is selectively subjected to a screen printing method in a region where it is not desired to form an inorganic protective film, specifically, on the upper surface of the die 35 on which the semiconductor chip is mounted and on the connecting portion 39 of the lead section, so that a cover 43 of organic resin such as epoxy resin or polyimide is formed thereon, as shown in FIG. 3B, by the screen printing method.

Subsequently, as shown in FIG. 3C, a protective film of an inorganic material, such as silicon nitride, silicon oxide, silicon carbide, or DLC, is formed over the entire lead frame by a plasma CVD or sputtering method (which will later be explained in detail). The inorganic material must show no qualitative changes when held for one hour in air at 500° C., must be heat-resistant, and must be resistant to oxidation. For this reason silicon nitride or silicon carbide are particularly superior for this application.

Next, the entire body is immersed in an organic solvent such as acetone or NMP (N methyl 2 pyrrolidone) and treated with ultrasonic waves to dissolve the organic material 43 to be removed, while at the same time the covering protective film thereon is removed by the lift-off method. The lead frame of the present invention as shown in FIG. 3D is manufactured in this manner.

The cross section A-A' of the lead frame of FIG. 4A corresponds to the lead frame shown in FIGS. 3A to 3D. FIG. 4A shows the smallest single unit of the lead frame, while FIG. 4B shows a plurality of these units (5 to 25) assembled in a single substrate. (N.B. This assembly is also called a lead frame. However, to avoid confusion, it will be referred to here as a substrate). For simplicity, the right side of FIG. 4A has been partly omitted. As shown in FIG. 4C, 5 to 300 units of the substrate 47 are integrated by means of a jig 49 to give one substrate board 51.

FIG. 4C shows one part of the cross section, viewed from the side of the substrate board 51. On this substrate board 51, the protective film is formed as shown in FIG. 3 by the method detailed later. The part 53 in FIG. 4C corresponds to the part 53 shown in FIG. 4A.

FIG. 5 shows an exterior view of a plasma CVD device for forming a nitride film on the surface of the substrate board 51. In FIG. 5, a preparation chamber 57 is provided beside a reaction chamber 55 with a gate valve 61 positioned between them. A reaction space is enclosed by a frame-structured holder 69, a supply side hood 65a and a discharge side hood 65b. A gate valve 59 is provided so that the substrate board 51 can be placed in or removed from the preparation chamber 57. Five to fifty units of the substrate board 51 shown in FIG. 4C (FIG. 5 shows seven units) are positioned in positive polarity in the reaction chamber 55. A gas introduction system 73 is provided, such that argon gas for a plasma treatment is introduced by means of a line 75, nitrogen or ammonia by means of a line 77, then a silicon chemical compound vapor, for example, disilane (Si₂ H₆) by means of a line 79 through a flowmeter 81 and a valve 83 for each line into the reaction chamber 55 by means of a gas introduction port 63.

First, a vacuum of 1×10⁻³ to 1×10⁻⁸ Torr, and preferably 5×10⁻⁴ Torr to 1×10⁻⁸ Torr, is drawn on the reaction chamber 55 using a turbo-molecular pump and maintained from 5 to 15 minutes. In this way, the undesirable vapors throughout the adhesive are drawn out and quickly exhausted to the outside. Next, a reactive gas (here, a mixture of disilane and nitrogen gas in the ratio of disilane to nitrogen gas=1:5) is introduced through the gas introduction port 63, passes through the supply side hood 65a, and through a nozzle 67a into a space in the reaction chamber 55 enclosed by a frame-structured holder 69, the hood 65a and the hood 65b. Here, electric power of 1 kilowatt and 13.56 MHz was supplied to a pair of electrodes 85a, 85b provided on the inside of the supply side hood 65a and the discharge side hood 65b. A film of a thickness of 300 to 5000 Å is formed at a temperature from room temperature to 300° C., generally a film of a thickness of 1000 Å (1000 Å±200 Å) is formed at an average deposition rate of about 3 Å/sec for about 10 minutes.

The silicon nitride film formed in this manner in an example had a dielectric strength of 8×10⁶ V/cm or greater and the specific resistance was 2×10¹⁵ Ωcm. The infrared absorption spectrum in the example showed a Si-N bond absorption spectrum of 864 cm⁻¹, and the refractive index was 2.0.

Reliability tests were then performed on three hundred of the electronic devices using the lead frame of the present invention as shown in FIG. 2, where the electronic devices were stored under 85° C./85% RH continuous for moisture absorption by the plastic molding, then heated at 260° C. for 3 sec. The results are shown in the following table.

    ______________________________________                                                Film Thickness Absorption Ratio                                         No.    Å          (Wt %)       Cracks                                      ______________________________________                                         1      200            0.248        0/20                                        2      500            0.251        0/20                                        3      1000           0.238        0/20                                        4      500            0.241        0/20                                        5      2000           0.250        0/20                                        6      No Film        0.259        20/20                                       ______________________________________                                    

As indicated in the results No. 1 to No. 5, there were no defective samples, specifically none of twenty samples were defective, where the protective film was formed. In the case of No. 6, where no protective film was formed, out of twenty samples all were defective.

In this embodiment, the cover film which covers the conductive section may be made of an inorganic material, and the forming method used may be the sputtering method, ion plating method, or other physical film forming methods. The die of the lead frame of this embodiment is positioned lower than the lead, so that the surface of the electronic part and the surface of the lead were made almost the same height, but it is acceptable to coat the lead frame having a previously provided flat surface with an inorganic material and then indenting the die section downward. In addition, it is acceptable to form an opening 32 as shown in FIG. 2 to compensate for the heat distortion.

The present invention is not limited to the preferred embodiment. For example, the present invention can e applied to a hybrid IC provided with a metal and a condenser are attached. Also, not only wire-bonding, but flip chip bonding or solder bump bonding can be used. 

What is claimed is:
 1. An electronic device comprising:a lead frame; a device proper mounted on the lead frame; wiring for making electrical contacts between said device proper and lead frame; and a package enclosing the lead frame and the device proper, said lead frame being coated with an inorganic film except for said device proper and said wiring electric contacts.
 2. The electronic device of claim 1, wherein said inorganic film is selected from the group of silicon nitride, silicon oxide, silicon carbide and DLC (Diamond-Like Carbon).
 3. A leadframe for mounting a semiconductor chip thereon having a conductive surface, wherein said leadframe is covered with an inorganic film except for a portion on which an electrical contact will be made.
 4. The leadframe of claim 3 wherein said inorganic film is selected from the group consisting of silicon nitride, silicon oxide, silicon carbide and diamond-like carbon. 